Slip White injection molding Veles LE analog Chaika, PFL 2
Designed for the manufacture of porcelain products by the method of slip casting into gypsum molds
A month of maturation, magnetic separation and three-fold sieve enrichment took place at the production of the slip.
A complex of electrolytes was added to the slip to achieve rheological properties, and also underwent a nine-hour deaeration,
The product is completely ready for use
If you have any questions about the use, call us, our technologist will advise you.
Bottled in containers at the customer's choice. The cost of the container is paid separately.
Properties
The suspension density is 1,67-1,71 kg/dm3;
The humidity of the suspension is 34-35% (when filling flat products with a liquid method, an increase in humidity to 36% is recommended);
Calculated TCLR, α 10ˉ⁷, in the range of 20 - 400 ° C - 61;
Full shrinkage – 11,5-14% (depending on the temperature and firing mode);
Water absorption – 4,7-2,8% (depending on the temperature and firing mode);
Recommended firing temperature:
The temperature is 800-900 ° C;
Watered – 1180-1220 ° C.
Designed for the manufacture of porcelain products by the method of slip casting into gypsum molds
A month of maturation, magnetic separation and three-fold sieve enrichment took place at the production of the slip.
A complex of electrolytes was added to the slip to achieve rheological properties, and also underwent a nine-hour deaeration,
The product is completely ready for use
If you have any questions about the use, call us, our technologist will advise you.
Bottled in containers at the customer's choice. The cost of the container is paid separately.
Properties
The suspension density is 1,67-1,71 kg/dm3;
The humidity of the suspension is 34-35% (when filling flat products with a liquid method, an increase in humidity to 36% is recommended);
Calculated TCLR, α 10ˉ⁷, in the range of 20 - 400 ° C - 61;
Full shrinkage – 11,5-14% (depending on the temperature and firing mode);
Water absorption – 4,7-2,8% (depending on the temperature and firing mode);
Recommended firing temperature:
The temperature is 800-900 ° C;
Watered – 1180-1220 ° C.
Рекомендации по уходу
Firing interval: 1200°C - 1250°C.
AIR SHRINKAGE: 3,5%
TOTAL SHRINKAGE AT 1200°C: 12,5%
Water absorption AT 1200°C: 1,5% /- 0,5%
The humidity of the slip is from 30 to 33%
AIR SHRINKAGE: 3,5%
TOTAL SHRINKAGE AT 1200°C: 12,5%
Water absorption AT 1200°C: 1,5% /- 0,5%
The humidity of the slip is from 30 to 33%